Describe
FAQ

AISI 1010 square tube

AISI 1010 carbon steel is a plain carbon steel with 0.10% carbon content. This steel has relatively low strength but it can be quenched and tempered to increase strength.

AISI 1010 chemical composition

Fe	Mn	S	P	C
99.18-9.62%	0.30-0.60%	<=0.05%	<=0.04%	0.08-0.13%

Heat Treatment of AISI 1010 Normalize at 1725° to 1775°F (941° to 968°C) before air cooling Anneal at 1650° to 1750°F (899° to 954°C) before furnace cooling Harden at 1650° to 1700°F (899° to 927°C) before quenching in water, brine or caustic Can be case hardened AISI 1010 square tube mechanical properties

Properties		Conditions
Properties		T (°C)	Treatment
Density (×1000 kg/m3)	7.7-8.03	25
Poisson's Ratio	0.27-0.30	25
Elastic Modulus (GPa)	190-210	25
Tensile Strength (Mpa)	365	25	cold drawn (round bar (19-32 mm))
Yield Strength (Mpa)	305
Elongation (%)	20
Reduction in Area (%)	40
Hardness (HB)	105	25	cold drawn (round bar (19-32 mm))

Hot Working

The hot working capacity of AISI 1010 carbon steel is between the ranges of 482 to 930C (900 to 2000F).

Cold Working

The cold working capacity of AISI 1010 carbon steel is good. In cases where severe cold working is performed stress relief or full anneal has to be performed.

Quotations:

FOB/CFR/CIF
Products Inspection:

Issued Original Mill test certificate
Products Service:

Shot blasting and Painting, Cutting, welding and so on
Shipside:

Qingdao, Shanghai, Tianjin, ect.